Undoped InP epilayers with high purity were grown by using $In/PCl_3/H_2$ chloride vapor phase epitaxy. It was found that the growth of InP homoepitaxial layer is optimized at the growth temperature of $630^{circ}C$ and at the $PCl_3$ molar fraction of $1.2 imes10^{-2}$. The carrier concentration of InP epilayer was less than $10^{14} {cm}^{-3}$ from the low temperature (11K) photoluminescence measurement. Growth behavior of undoped InP current blocking layer on reactive ion-etched (RIE) mesas has been investigated for the realization of 1.55 $mu extrm m$buried-heterostructure laser diode (BH LD), using chloride vapor phase epitaxy. On the base of InP homoepitaxy, InP current blocking layers were grown at the growth temperatures ranging from $620^{circ}C$ to $640^{circ}C$. Almost planar grown surfaces without edge overgrowth were achieved as the growth temperature increased. It implied that higher temperature enhanced the surface diffusion of the growth species on the {111} B planes and suppressed edge overgrowth.