Compressive strength reduction characteristics of 4 different linerboards(SC, KA, SK and IK) as influenced by temperature and humidity were investigated by ring crush test. No significant effect of temperature on the reduction of compressive strength was found for samples prepared at 5$^{circ}C$ and 30$^{circ}C$. At the relative humidity of 66 percents, IK linerboard showed the lowest reduction of the compressive strength. At the relative humidity of 93 percents, KA linerboard lost 40 percents of its initial compressive strength while SK linerboard lost its strength up to 56 percents. The result indicated that KA linerboard was the most cost effective and material with the highest compressive strength among tested linerboards.