The main objectives of this research are to experimently explain the drilling mechanism for the production of bad holes and good holes during the drilling operation, to investigate how a wide range of drilling parameter affect composite laminate strength reduction, and to find which type of test provides the greatest interrogation of notched composite laminates. To achieve these objectives, a bulk of test specimens have been drilled with 5 different drilling parameters and tested with compressive, tensile, and flexural loads. It was found that the drilling parameters had a measurable effect on specimen hole quality as measured by static strength. The specimens, which were well supported, which had the higher spindle speed and lower feed rate, and which were well clamped gave the best hole qualities. The flexural test results presented the most clear and consistent failure strengths relating to the drilling parameters and associated hole quality.