The surface of Alloy 600 was alloyed using a continuous wave $CO_2$ laser beam in order to improve its corrosion resistance. Laser surface alloying (LSA) was done by melting the surface electroplated with Cr of the alloy. The Cr concentration of the alloyed surface was 28-30 at.%, which is similar to that of Alloy 690. Alloying elements in the alloyed layer was observed to be distributed very homogeneously all over the alloyed region. According to the electrochemical and modified Huey tests, the corrosion resistance, in particular the grain boundary corrosion resistance, of the LSA specimens was significantly improved, compared with that of the as-received(AR) specimen. This improved corrosion resistance of the alloyed specimen might be attributed to the high Cr content which could make possible formation of more stable and dense passive film onto its surface.