The laser induced forward transfer(LIFT) technique employs a pulsed laser to transfer parts of a thin metal film from an optically transparent target onto an arbitrary substrate in close proximity to the metal film on the target. In this work, a two-step method, the combination of LIFT process, in which a Au film deposited on the $Al_2$O$_3$ substrate by Nd:YAG laser and subsequent Au electroless metal plating on the by LIFT process generated Au seed, was presented. The influence of laser parameters, wavelength, laser power, film thickness and overlap ratio of pulse tracks, on the shapes of deposit and conductor line after electroless plating is experimentally studied. As a results, the threshold power densities for ablation, deposition and metallization were determined and comparison of threshold value between the wave length 1064nm and the second harmonic generated 532nm. In odor to determine a possible application in the electronic industry, a smallest conduct spot size, line width and isolated line space were generated.