The surface characteristics of nitrogen ion implanted iron aluminides were investigated using various electrochemical methods in $H_2$$SO_4$+KSCN and HCl solutions. Nitrogen ion implantation was performed with doses of $3.0$ imes$10^{17}$</TEX> /ions/$ extrm{cm}^2$ at an energy of 150keV. Nitrogen ion implanted iron aluminides increased the corrosion potential and significantly decreased grain boundary activation, the active current density, and passive current density. Nitrogen implanted iron aluminides with Mo increased the corrosion, pitting potential, repassivation potential and │$E_{pit}$-$E_{corr}$│ value. Whereas, implanted iron aluminides containing boron reduced the pitting and repassivation potential in comparison with nitrogen implanted iron aluminides with Cr and Mo.o.