Welding is a reliable process and is mainly adopted for fabricating heavy structures. Recently, transverse cracks in the weld metal is serious problem, and they affect cost, efficiency, safety and joint reliability for various welded structures. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained are as follows; 1) The content of diffusible hydrogen in the commercial flux cored are welding wire was remarkable change by manufacturer. 2) The diffusible hydrogen content was thd main factor for weld metal transverse cracks. 3) Weld metal was immune to transverse cracking under the condition of low diffusible hydrogen content of high restraint condition. 4) The factors for weld metal transverse crack would be the content of diffusible hydrogen and restraint of weld joint.