According to repeated measurements and correction procedures, the accuracy of the phase-shifting profilometry was developed. At first, after 20 final models for maxillary complete denture were duplicated , the mucosa sur-faces of models were measured with the phase-shifting proflometry and each mirror view of these was calibrated. Maxillary casts were divided into 4 groups of 5 casts per each, and wax dentures with 2 sheets of baseplate wax and artificial teeth were made and then cured according to the curing method of each group. Group I ; quick curing with QC-20 acrylic resin Group II ; 9 hour curing with QC-20 acrylic resin Group III ; SR-Ivocap system Group IV ; metal base and quick curing with QC-20 acrylic resin. After curing, polishing, and storing at $37^{circ}C$ in saline for 30 days, the forms of the impression surface of the dentures were measured with the phase-shifting profilometry. Then, the impression surface form of each denture was placed in the optimal position of com-parison with the mirror view of the same final cast. The amount and direction of distortion of each denture was analyzed and the effects of polishing and storage in each denture were compared, The obtained results were as follows : 1. In Group I, the denture was observed as the appearance distorted in the opposite direction of the mucosa and the postero-lateral part of palatal portion of the denture was observed as the appearance separated from the mucosa. Also, the buccal flanges of the denture were observed as the appearance distorted in the direction of the mucosa. 2. In Group II, the postero-lateral part of palatal portion of the denture was observed as the appearance separated slightly from the mucosa. The bilateral buccal flanges of denture were observed as the appearance distorted severely in the direction of the mucosa. 3. In Group III the bilateral part of the residual ridge crest portions and the buccal flanges of the denture were observed as the appearance distorted in the direction of the mucosa, and specially, the buccal flanges of the maxillary tuberosities were distorted severely. 4. In Group IV, the acrylic resin base of the buccal portion of the denture was observed as the appearance distorted in the opposite direction of the mucosa. 5. The phase-shifting profilometry, done with repeated measurements and correction procedures, was effective in comparing the amount and direction of distortion at every position after the laboratory work and the delivery of maxillary complete denture.