The purpose of this study was to evaluate the effect of wattage and curing time on surface hard-ness, three-point bending strength and internal porosity of microwave curing denture base resin. Two sizes of resin specimens were made of Acron $MC^{(R)};;;3.5{ imes}10{ imes}60mm$ for surface hardness and three-point bending strength measurement and $5{ imes}12{ imes}60mm$ for internal porosity measurement. They were cured by microwave energy at varing wattages(500W, 700W) and curing times(2min., 3min., 4min.) to determine if a certain wattage/curing time combination would improve physical properties. Surface hardness was measured with Vikers hardness tester, three-point bend-ing strength with universal testing machine and internal porosity was calculated by measuring the weight in air and in water. The results obtained were as follows: 1. There was no significant difference in percent porosity among experimental groups(p>0.05). 2. 500W/3min. group showed the higher surface hardness than 700W/2, 3, 4min. groups(p<0.05), and 700W/4 min. group showed the lower surface hardness than 500W/2, 3, 4min. groups(p<0.05), but there was no significant difference among others(p>0.05). 3. 500W/3min. group yielded the higher value of bending strength than 500W/2min., 700W/3, 4min. groups(p<0.05), but there was no significant difference among others(p>0.05).