A new 5th generation adhesive system(ONE-STEP) has been supplied which operators can apply to conditioned tooth surfaces by one simplified step. The purpose of this study was to determine whether different methods of adhesive application and various air drying duration after applying adhesive affect the shear bond strength of composite resin to dentin, and to evaluate the adhesive pattern of composite resin and dentin under SEM. Seventy-seven extracted human molar teeth were cleaned and mounted in palstic test tubes. The occlusal dentin surfaces were exposed with Diamond Wheel Saw and smoothed with Lapping and Polishing Machine (South Bay Technology Co., U.S.A.). Teeth were randomly divided into 7 groups (n=11), In experimental A group, adhesive was applied to dentin with agitation for 20 sec. In experimental N-A group, adhesive were continuously applied to dentin for 20 sec. Also control and experimental 1, 2, 3, 4 groups were dried for 10, 0, 5, 20, 30 seconds after applying adhesive, respectively, Adhesives were light cured for 10 sec. A gelatin capsule 5mm in diameter was filled with Aelitefil$^{TM}$ composite resin, placed on the treated dentin surface and light cured for 40 see, from three sides, All specimens were stored in distilled water at room temperature for 24 hours. The shear bond strengths were measured using a universal testing machine(AGS-1000 4D, Japan) at a crosshead speed of 5mm/min. An one-way ANOVA and LSD test were used for statistical analysis of the data. For SEM evaluation, seven specimens were made and sectioned. Representive postfracture and seven specimens were mounted on brass stubs, sputter-coated with gold and observed under SEM. The results were as follows : 1. The shear bond strength of experimental A group which adhesive were applied to dentin with agitation was higher than that of experimental N-A group (continuous application), and there was significant difference between two groups (p<0.01). 2. The interface between composite and dentin according to different application methods showed close adaptation in experimental A group and showed tinny gap in experimental N-A group. 3. The shear bond strength accoding to various air drying duration was the lowest value(7.57${pm}$2.60 MPa) in experimental 1 group, so there was significant difference between experimental 1 group and other four groups (p<0.05). But there was no significant difference of shear bond strength between four groups (p>0.05). 4. The interface between composite and dentin according to various air drying duration showed close adaptation in control group and tinny gap in experimental 3 and 4 groups. But experimental 1 and 2 groups showed $30{mu}$ and 6 - $10{mu}m$ thick gaps, respectively.