The purpose of this study was to investigate the thermal resistance and the liquid/vapor water transfer characteristics of four waterproof and water vapor permeable coated fabrics with the ground fabric called nylon taffeta. In order to establish the experimental environment, outdoor temperature and humidity in Taegu during the last three years were examined and the experiment was performed at (1) $15^{circ}C$, 50% R.H., (2) $20^{circ}C$, 60% R.H., (3) $25^{circ}C$, 65% R.H., which were the average standards in spring and fall. The test results were as follows ; 1. Among physical parameters, the thinner the thickness was, the higher the water vapor permeability was. But the porosity in thickness was not proportional to water vapor permeability linearly. 2. The thicker the thickness of specimens was and the smaller the bulk density and porosity were, the higher the thermal resistance. And the results also shown that the larger the temperature difference between the environmental temperature and the hot plate was, the more the difference of CLO values was apparent. 3. Since the contact angle of all specimens are above $90^{circ}$, the all specimens have a good performance in waterproof. The more the specimens surface were rough, the higher the thermal resistance was. 4. According to the result of performing moisture transfer test using the simulating body skin-clothing-environment system, the humidity sensor placed in between the fabric and the environment detected the full saturation in 10 minutes after the experiment had began at $15^{circ}C$, 50% R.H. and in 15 minutes after the experiment both at $20^{circ}C$, 60% R.H. and at $25^{circ}C$, 65% R.H. 5. ${Delta}$ values of the humidity sensors placed in between the human body and the fabric and in between the fabric and the environment fluctuated repeatedly within the range of $20{sim}40%$ at $20^{circ}C$, 60% R.H., and $15{sim}30%$ at $25^{circ}C$, 65% R.H.