Fatigue crack growth behaviors of Cr-Mo steels developed recently for thick-wall pressure vessel were investigated. Experiments in accordance with ASTM E647 standard were performed for 1/2 inch CT specimens of $2^(1/4)$Cr-1Mo and 3Cr-IMo steels in gaseous environments, hydrogen gas of 10 atm, 1 atm and argon gas of 1 atm. Fatigue crack growth rates were observed and effects of gaseous hydrogen and argon on the crack growth behavior were discussed.