목재는 2-메타크릴로일옥시에틸 이소시아네이트(MOI)와 $50-60^{circ}C$에서 촉매존재하에서 매우 쉽게 반응하였다. 적외선 분광분석을 통하여, 목재가 MOI와 우레탄결합($1715cm^{-1}$)를 형성하고 있을 뿐만 아니라, 올레핀구조의 탄소간 이중결합 ($1635cm^{-1}$)이 존재하고 있음이 밝혀졌다. 도입된 메타크릴산기는 다른 비닐모노머와의 그래프트공중합시 반응시점으로 작용할 것이다. 또한 MOI처리목재는, MOI와의 반응에 의해 친수성이던 목재의 표면이 소수화되어 접촉각이 증대되는 결과를 낳았다. X선광전자분광분석(XPS)의 결과, 목재의 표면부위의 대부분은 MOI에 의해 개질되었음을 밝혀졌다.
This study was carried out to introduce functional groups onto wood by reacting with 2-methacryloyloxyethyl isocyanate(MOI). The effects of the catalyst and the reaction conditions(temperature and time) on the treatment were investigated. The evidence of bonding between wood and MOI were examined by infrared(IR) spectroscopy. The change in surface characteristics of MOI treated wood was examined by water contact angle measurement and X-ray photoelectron spectroscopy(XPS). Wood reacted quickly with MOI in the presence of di-n-butiltin dilaurate catalyst. Especially, the increase in weight percent gain(WPG) with increasing in reaction time was remarkable at the reaction temperature of over $50^{circ}C$. The IR spectrum of wood reacted with MOI showed a strong urethane absorption(1715 $cm^{-1}$) but no isocyanate(2235 $cm^{-1}$) absorption. It also showed a sharp olefinic C=C double bond absorption at 1635 $cm^{-1}$. This means that an introduced methacrylate group becomes the starting point of further graft copolymerization with another vinyl monomers. The wood modified with MOI showed a gradual increase in contact angle with increasing in WPG, which means that the hydrophilic wood surface become quite hydrophobic. Also, it was cleared that most parts of the wood surface were modified with MOI by XPS analysis.