A thermal aging is observed in a primary reactor cooling system(RCS) made of a casting stainless steel when the RCS is exposed for long period at the reactor operating temperature, 290~3300C An investigation of effects of thermal aging on a low cycle fatigue characteristics included a stress variations caused by a reactor operation and trip, is required. The purpose of the present investigation is to find an effect of a thermal aging of the CF8M on a low cycle fatigue life. The specimen of CF8M are prepared by an artificially accelerated aging technique holding 300 and 1800hr at 4300C respectively. The low cycle fatigue tests for the virgin and two aged specimens are performed at the room temperature for various strain amplitudes($varepsilon$ta), 0.3, 0.5, 0.8, 1.0, 1.2 and 1.5% strain. Through the experiment, it is found that the fatigue life is rapidly reduced with an creasing of the aging time. The experimental fatigue life estimation formulas between the virgin and two aged specimen are obtained and are proposed to a analysis purpose.