The fretting wear corrosion characteristics between the SM20C and the SM20C, the YBsC3 and the STC4H was experimented by using radical type friction experimental device under the corrosion environment of atmosphere, neutral solution, acid solution and chemical factors of the sea water. The affection of underground water that affect fretting wear corrosion of the SM20C which is moving specimen was more sensitive at the STC4H and more insensible at the YBsC3. The affection of underground water that affect fretting wear corrosion of the STC4H was less, but in the $0.5\%;H_2SO_4$ and $0.5\%;HNO_3$ solutions the fretting wear corrosion of the STC4H was more large. The fretting wear corrosion of the SM20C which is moving specimen in the underground water was less than in the $3.5\%;NaCl$, $0.5\%;H_2SO_4$ and $0.5\%;HNO_3$ solutions. As time passed, the fretting wear corrosion is increased in the $HNO_3$ solution and dull in the $0.5\%;H_2SO_4$ solution.