Cycle life test was carried out to evaluate the failure modes of the gel type nth batteries at $C_5$ currents and $100\%$ DOD. When the batteries were charged at constant voltage of 2.40 V and 2.50 Vi respectively, cycle lift was over 1,000 cycles. The batteries lost 426.4 g and 391.2 g of electrolyte far each case after the weight measurement. The battery charged at 2.50 V was shown to have a better cyclic performance than charged at 2.40 V, and the amounts of electrolyte loss was proportional to charge factor. After cycle test, the micro-structure of positive active material was completely changed and the corrosion layer of positive grid was about $50{mu}m$. Failure mode of the positive plate of the gel type battery was a shedding of the positive active material, and the cause of discharge capacity decrease was found to be a electrolyte loss.