Ni tapes were textured by taking advantage of their secondary recrystallization. The obtained 18cm long tapes had textures of single crystalline qualities with their [001] axes tilted with respect to the surface and their [010] axes parallel to the rolling direction. The reproducibility of this texturing was checked by taking statistics on the crystal orientations of 24 Ni tapes. $YBCO/CeO_2/YSZ/CeO_2$ films grown on the Ni tape had the same crystalline orientations. Magnetic field dependent I-V relations were measured on a 5cm section of the tape. $J_c$ defined by $20{mu}V/mm$ criterion was $1.5 imes10^5A/cm^2$ at 77K under zero field and was reduced by $sim$50% under the applied magnetic field of 5T.