The mechanism of the blowhole and the pit formation in lap-jointed fillet Co₂arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows: 1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage. 2) Most of the pits was back-filled at the last stage of their formation.