The wear behavior of thermal sprayed AlSiMg-40TiC composite coatings were studied as a function of load and sliding velocity under unlubricated conditions. Experiments were performed using a block-on-ring(WC-6wt%/Co, Hv 1500) type. The tests were carried out a various load(30∼ 125.5N) and sliding velocity(0.5∼2.0m/s). Three wear rate regions were observed in the AlSiMg-40TiC composite coatings. The wear rate in region I at low load (less then 8N( were less than 1×{TEX}$10^{-5}${/TEX}㎣/m. Low wear rates in region I resulted from the load-bearing capacity of TiC particles. The transition from region I to II occurred when the applied load exceeded the fracture and pull-out strength of the particles. The TiC fractured particles trapped between the specimen and the counterface acted as third-body abrasive wear. The subsurface layer worn surface in region II was composed of the mechanically mixed layer (MML). The wear rate increase abruptly above a critical load (region III). The high wear rate in region III was induced by frictional temperature and involves massive surface damage.