Dielectric property of Ba-modified 0.65Pb(Mg1/3Nb2/3)O3-0.35PbTiO3 ceramics having compositions near the morphotropic phase boundary was investigated. For the specimens having Ba contents between 0 and 20 at%, the average transition temperature was decreased linearly with increasing Ba contents and the degree of hysteresis was also decreased with increasing Ba contents. The maximum dielectric constants (K), electric field induced polarization(P) and electrically-induced strain(S) were found to exihibit a maximum value at∼3 at% of Ba. The increase of S and the decrease of hysteresis by minor additions of Ba impurities indicated the development of new higher perfomance actuator materials. The composition of Ba-PMN-PT (10/65/35) may be appropriate for capacitor materials because of low hysteresis and high polarization.