Er-doped sodiumborosilicate glass films for waveguides amplifier were fabricated by Aerosol Flame Deposition(AFD) method. Al2O3 was added to sodium borosilicate glass films to suppress the formation of crystalline phase and control the refractive index. the formation of crystalline phase was suppressed above Al2O3 of 6 wt%. As the amount of Al2O3 increased from 2 to 12 wt% the refractive index of glass films increased lineary from 1.4595 up to 1.4710. After the core of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3＋8wt%Er2O3 was coated on the buffer layer of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3, the core was etched by reactive ion etching. The absorption spectrum of 3 cm waveguide amplifier showed two peaks of 1530 and 1550 nm.