Six different SiC ceramics with SiO2-Re2O3 (Re=Yb, Er, Y, Dy, Gd, Sm) as sintering additives have been fabricated by hot-pressing the SiC-Re2Si2O7 compositions at 1850$^{circ}C$ for 2 hr under a pressure of 25 MPa. The room temperature strneth and the fracture toughness of the hot-pressed ceramics were characterized and compared with those of the ceramics sintered with YAG (Y3Al5O12). Five SiC ceramics (Re=Yb, Er, Y, Dy, Gd) investigated herein showed sintered densities higher than 94% of theoretical. Tthe SiC-Re2Si2O7 compositions showed lower strength and comparable toughness to those from SiC-YAG composition, owing to the chemical reaction between SiO2 and SiC during sintering. SiC ceramics fabricated from a SiC-Y2Si2O7 composition showed the best mechanical properties of 490 MPa and 4.8 MPa$.$m1/2 among the compositions investigated herein.