In this study, we chose the basic composition which indicated the best electrical properties by change of x content(0, 0.05, 0.1, 0.15, 0.2, 0.25 mol respectively) in xPb(Mn1/3Sb2/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 ceramics. And we substituted Cd2+ for Pb2+ site, then observed the sintering behavior, microstructure and electrical propertties according to the various sintering temperature. The basic composition was the 0.05PMS-0.95PZt, and it showed single perovskite phase and excellent properties. In case of Cd2+ substitution, we were able to sinter at 90$0^{circ}C$ which was lower than conventional sintering temperature(1200~130$0^{circ}C$). Especially, when the 2mol% substituted PMS-PZT specimens were sintered at 90$0^{circ}C$ for 2h, we obtained the p=7.6g/㎤, kp=56%, Qm=520 and made sure of a position of Cd2+ substitution by observing lattice parameter, phase transition temperature. From this results, we could infer that because Cd2+ substituted fro A-site, low temperature sintering of Cd2+ substituted PMS-PZT without any loss of electrical properties shows its applicability for the piezoelectric ceramic transformer.