This dissertation is focused on the study over the improvement for the early strength of belite-rich cement(BRC). For this purpose, the initial hydration behaviors according to addition of different calcium sulfate types were evaluated. From the observations by XRD, DSC and SEM, the BRC II and III with the addition of natural anhydrate and flue gas desulphurization(FGD) gypsum, respectively, formed much ettringite after 7 days more than the BRC I with the addition of chemical gypsum. The compressive strength of the BRC II and III developed outstandingly due to the formation of calcium aluminate hydrate within pores of hardened BRC paste. Especially, in the case of BRC III adding FGD with low impurities, the early as well as long term compressive strengths were shown very high, compared with other specimens.