Effect of catalysts, which was catalyzed by acid(HCl and HNO3) and base(NH4OH), on characteristics of the mullite powders prepared by sol-gel methdo wa sinvestigated by XRD, TGA, SEm AND BET. As a result, weight loss as a function of catalysts was in order of HCl=32.6%>HNO3=25.44%>Non=24.0%>NH4OH=22.5%. The mullite powder dried at 100$^{circ}C$ appeared spherical shape in acid catalyst and different shape in base catalyst, but sintering powder at 1400$^{circ}C$ appeared very fine particle of 0.05∼0.1$mu extrm{m}$ regardless of catalysts. In all cae, the pore quantity, which was capable to adsoprtion, was decreased with increasing temperature. In base catalyst, no change of special surface area in mullite appeared.