We have investigated the feasibility of spin on glass (SOG) film from polysilazane-type resin as a premetal dielectric (PMD) layer of the next-generation ultra-large scale integrated (ULSI) devices. A commercial polysilazane resin and a polysilazane-type resin with oxidizing agent were spin-coated and cured to form SOG films. In order to study the effect of oxidizing agent and annealing, the SOG films were characterized as cured and after annealing at $400^{circ}C$ to $900^{circ}C$. the density and the resistance against wet chemical of the SOG films were improved by the addition of oxidizing agent, because oxidizing agent enhanced the conversion from polysilazane polymer to $SiO_2$. The hole profile issue associated with insufficient curing of polysilazane in narrow gaps was also resolved by oxidizing agent, while the gapfill capability of SOG was not deteriorated by oxidizing agent.