(YbxY1-x)Ca₄O(BO₃)₃ single crystals where x=0.3,8,15,20% were grown by Czochralski Method. The crystals grown under the optimum conditions were transparent and colorless with good crystal form. Using polarizing microscope, crystal defects such as parasite crystals and bubbles were detected depending on the composition of melts and pulling rates. The optimum growth parameters for high quality of single crystals were 15∼20 rpm of rotation rate and 2mm/h of pulling rate at the flow rate of 2 l/min of Nitrogen gas. The relationship between crystal axes and optical axes was investigated by optical crystallographic method, polarization technique and single crystal X-ray method. From the spectroscopic measurements, it was confirmed that there were strong absorption bands at 900 and 976.4 nm and strong emission band at 976.4 nm in Yb3+ ion doped YCa₄O(BO₃)₃ crystal. For the application of second harmonic generation of 1.064 ㎛ laser, non-linear optical devices with θ=32.32° and Ψ=0°, λ/10 of flatness and the size of 6x8x5.73 mm were fabricated from the grown YCa₄O(BO₃)₃ crystal.