In this paper we investigated the structural dielectric and piezoelectric properties of 0.03Pb(Sb$\_$1/2//Nb$\_$1/2/)-0.97Pb(Zr$\_$0.495//Ti$\_$0.505/)O$_3$+0.5 wt% excess PbO + wt% MnO(X=0, 0.1, 0.3, 0.5, 0.7) ceramics to develop the high-power piezoelectric transformer. The piezoelectric transformers with dimension of 27.5$ imes$27.5$ imes$2.5［mm$^3$］were fabricated and their electrical properties were measured. Maxima of piezoelectric properties such as electro-mechanical coupling factor of 0.534 and mechanical quality factor of 1487 were obtained for the PSN-PZT with 0.3wt% MnO. voltage step-up ratios of piezoelectric transformers at 500［Ω］and no load were 0.78, 12.82, respectively. The maximum efficiency of piezoelectric transformer was 98.6% at 800［Ω］. While the 14W fluorescent lamp were driven by the piezoelectric transformer for more than 20［min］, increment of temperature in the piezoelectric transformer was 7［$^{C}$］.