S $r_{0.9}$/B $i_{2.1}$/T $a_{2}$/ $O_{9}$ solutions was synthesized by MOD (metalorganic decomposition) method. SBT thin films with 2000$AA$ thickness were prepared on Ir $O_2$/ $SiO_2$/Si and Pt/Ti/ $SiO_2$/Si substrates using the spin coating process and then investigated the dielectric and electrical properties of them. In the case of using Ir $O_2$bottom electrode the hysteresis loop was saturated at lower temperature than Pt/Ti electrode but the breakdown phenomenon was occurred at low voltage because of the rough surface morphology and porous microstructure of SBT thin films. As the results of the fatigue and imprint characteristics related to the lifetime and reliability of devices after 10$^{10}$ cycles the fatigue rates were about 10% at the Ir $O_2$and Pt/Ti bottom electrodes. Both SBT thin films with Ir $O_2$ and with Pt/Ti bottom electrodes show a slight tendency to imprint after 10$^{9}$ cycles but do not lead to a failure.e.e.