When insoluble sericin was hydrolyzed by treatment of NaOH solution, the solubility was increased with higher treatment temperature and longer treatment time. Whereas it was decreased in addition of NaHSO$_3$. As the results of electrophoresis in sericin powder obtained by the NaOH treatment, a distinguishable band was not confirmed. Average degree of polymerizations(A.D.P.) of sericin hydrolyzed by NaOH solutions were about 19.6∼22.1 and average molecular weight(M.W.) were about 2,200∼2,500. The longer hydrolysis time increased the whiteness of sericin powder. As the results of amino acid analysis, the contents of Thr., Tyr., and Ser. were decreased in NaOH hydrolysis as compared to HCl hydrolysis. In DSC analysis, thermal deformation and pyrolysis peak located at near 230$^{C}$ and 320$^{C}$, respectively.