In this paper the residual stresses on lubricated sliding surfaces were measured during break-in procedure and up to scuffing by the X-ray diffraction method. The cylinder-on-disk type tribometer was used with the line-contact geometry. Scuffing tests were done using a constant load. In the break-in procedure the loads were increased from very low values in several steps. It was found that the sliding surfaces with break-in represented relatively higher values of residual compressive stresser than those without break-in. The residual stresses below the surfaces showed the small amount of stress increases. The results of scuffing tests with and without break-in showed the same trends as break-in tests did. However, in case of tests with break-in procedure the stresses below the surfaces showed very large increases in the residual compressive stresses. From the tests of break-in and scuffing, it was found that the increases in scuffing lives were related with the increases of residual stresses on the lubricated sliding surfaces with break-in.