This study discussed the mechanical properties such as bending and shear of polyester fabric treated with a several weight reduction machine. With the increase in the rate of weight loss, the bending rigidity of the warp and weft of treated fabric decreased regardless of the weight reduction machine. At 6.5% weight loss, the bending rigidity of warp and weft yarn decreased to $0.035;gfcm^2/cm$ and $0.017;gfcm^2/cm$, respectively, and these values show 54% and 94% of their untreated warp and weft. At same rate of the weight loss, the bending rigidity of polyester fabric treated with C.D.R slightly higher than that of the tank type or liquor-flow type. On the other hand, below 6.5% weight loss, the shear rigidity of the warp and weft of the treated fabric rapidly decreased. But with the increase in the above 6.5% rate of weight loss, the decreasing tendency of the shear rigidity declined. At same rate of the weight loss, the shear rigidity of fabric treated with tank type nearly equal to the that of the liquor flow type. But at same rate of the weight loss, the shear rigidity of the fabric treated with C.D.R type higher than that of the tank or liquor-flow type.