Some physical characteristics as thickness swelling, heat conduction, and bending properties of composite hoards made of waste wood chip and charcoal were measured. Wood-charcoal composite boards of three types and cement board were prepared for this study as shown in Table 1, Keeping duration of strawberries in the boxes($25cm{ imes}25cm{ imes}25cm$) manufactured with the boards was also examined. Thickness swelling and bending properties(MOR and MOE) of board B and C were lower than those of board A. Among the wood-charcoal composite boards except cement board, there were no differences in heat conduction(mm/sec.). Strawberries in the box with board C were kept longer duration in fresh condition than that with cement board. From the results, it is suggested that wood-charcoal composite boards can be used for eco-material.