$Li_{0.44}MnO_2$cathode material has high reversibility during lithium insertion processes and is not easily damaged through over-charging or over-discharging. $Mn_2O_3$is often present as an impurity phase, and reduce the electrochemical capacity of electrode because this phase is electrochemically inert. Adding of excess NaOH reduced the $Mn_2O_3$to the content under undetectable by X-ray diffraction. Because the capacity can be increased in the cathode materials with larger unit cell, some of the manganese was replaced with titanium having larger ion size, and powders with the formula $Li_{0.44}T_{iy}Mn_{1-y}O_2$(where y = 0.11, 0.22, 0.33, 0.44, and 0.55) was synthesized and characterized. A maximum reversible capacity of 150 mAh/g was obtained for $Li/P(EO)_8$LiTFSI/$Li_{0.44}Ti_{0.22}Mn_{0.78}O_2$cells in electrochemical potential spectroscopy (ECPS) experiments. Cells with the titanium-doped manganese oxides exhibited a fade rate of 0.12 % or less per cycle.