Polyenaminonitriles containing cycloaliphatic and aliphatic units were prepared by interfacial or solution polymerization reaction of p-bis(1-chloro-2,2-dicyanovinyl) benzene (1) with 4-aminobenzyl-amine, 1-(2-aminoethyl)piperazine, 2-(aminomethyl)pyrrolidine and 4-(aminomethyl)piperidine. The chemical structure of the polymers was confirmed through a syntheses of the model compound. The resulting polymers possessed inherent viscosities of 0.29∼0.62 dL/g and they were easily soluble in polar aprotic solvents and common organic solvents. Thermal properties of the polymers such as curability and stability were studied by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and infrared spectroscopy. The polymers exhibited a large exotherm in DSC analyses and underwent a curing reaction around 340-370$^{C}$ to form insoluble materials. The polymers showed 70-80% residual weight at 600 $^{C}$ under nitrogen.