Poly(p-hydroxybenzoate) (PHB)/poly(ethylene terephthalate) (PET) 8/2 thermotropic liquid crystalline copolyester, poly(ethylene 2,6-naphthalate) (PEN), and PET ternary blend was spun to fiber by melt spinninB process, and tensile properties of the fibers were measured. The matrix of the fibers, PET and PEN, were dissolved in ο-chlorophenol at 55$^{circ}C$ for 2 hours, and the liquid crystalline polymer fibrils were observed using a scanning electron microscope. Halpin-Tsai equation for modulus calculation of short fiber reinforced composite and the rule of mixture for continuous reinforcement composite were modified, and the tensile modulus were calculated and compared with experimental modulus. To minimize difference between the theoretical and the experimental moduli, dimensionless viscosity constant (K) was given and used to modify two equations. The theoretical tensile modulus using the newly modified equations presentel a similar to the experimental tensile modulus of composite, and the modified equations presented a unique way to determine the tensile modulus of the liquid crystalline polymer reinforced thermoplastic composites.