Purpose : To investigate osseointergration of titanium implants into the tibia of rabbits, which were fed a low calcium diet and irradiated. Materials and Methods : To prepare the experimental model, control group was fed a normal diet and experimental group was fed a low calcium diet for 4 weeks. And then, titanium implants were inserted into the tibia of each rabbit. Experimental group was subdivided into two groups; low calcium diet/non-irradiation group and low calcium diet/irradiation group. The low calcium diet/irradiation group was irradiated with a single absorbed dose of 15 Gy at the 5th postoperative day. At 12, 19, 33, 47, and 61 days after implantation (1, 2, 4, 6, and 8 weeks after irradiation), the bone formation in the bone-implant interface area was examined by light microscopy and fluorescent microscopy. Results and Conclusions: 1. In the control group, there began to form woven bone in the bone-implant interface area at 12 days after implantation. As the experimental time was going on, the amount of bone which was in contact with the implant was increased. 2. In the low calcium diet/non-irradiation group, there began to form woven bone in the bone-implant interface area at 19 days after implantation. Although the amount of bone which was in contact with the implant was increased as the experimental time was going on, the extent of increased bone was weak as compared with control group. 3. In the low calcium diet/irradiation group, there began to form woven bone incompletely in the bone-implant interface area at 19 days after implantation, but there were vascular connective tissues in the bone-implant interface area over the entire experimental period. 4. In the control group and low calcium diet/non-irradiation group, bone labeling bands were observed at 33 days after implantation, which suggests that the bone formation and remodeling was in process, but interstitial bone remodeling was not observed in the low calcium diet/irradiation group.