We prepared $SiO_2-Na_2O-R_mO_n$ thin films based on economics of water glass and investigated optical, mechanical properties of product thin films. Coating sol stabilized with 1 N HCl and 1 N $NH_4OH$, was fabricated by using water glass and calcium nitrate, and aluminum nitrate as starting materials. As-coated films on stainless steel, Si wafer and soda-lime-silica glass by spinning were finally annealed at 500, 750 and $900^{circ}C$. Micro hardness and nitrogen content in film surface of annealed films were measured by Knoop hardness tester and EDX, respectively. Field Emission Scanning Electron Microscope (FE-SEM) and UV-VIS spectroscopy were adopted to analyze surface morphology and thickness and reflectance of our films.