The purpose of this study was to investigate the effects of investing conditions on the marginal discrepancy of conical telescope outer crown with Co-Cr-Ti alloy(Dentitan) and to compare the marginal discrepancy and the retention force of outer crowns using different pattern materials(plastic foil, casting wax, pattern resin). To evaluate the effects of investing conditions on the marginal discrepancy, patterns with plastic foil were invested under three different liquid/powder ratio conditions using phosphate bonded investment(Univest-nonprecious): standard, 10% decreased and 10% increased. At each liquid/powder ratio condition, metal ring was lined with single or double layers of ceramic ring liner. The marginal discrepancy of outer crown at different investing conditions was measured by ${ imes}100$ compact measuring microscope(STM5, Olympus, Japan). For measurement of the marginal discrepancy and the retention force of outer crown using different pattern materials, the investing condition of 10% decreased liquid/powder ratio and double layers of ring liner was selected because this investing condition resulted in the best fit of outer crown. Marginal discrepancy was measured in the same way above and retention force on universal testing machine. Under the conditions of this study, the following conclusions were drawn: 1. The thickness of ring liner had more influence on the marginal discrepancy of outer crown than the liquid/powder ratio, and the acceptable marginal fitness could not be expected at the investing condition directed by investment manufacturer 2. There were no differences in the marginal discrepancy of outer crown among three different pattern materials(P>0.05). 3. Casting wax showed the greatest retention force(1640g) of outer crown, followed by pattern resin(1110g), plastic foil(820g). However, there was no significant difference between plastic foil and pattern resin(P>0.05). 4. Plastic foil showed the least variation in marginal discrepancy and retention force.