Intracoronal bleaching is currently disregarded by many clinicians because of the potential consequence of cervical resorption. To prevent this complication it is recommended that intra coronal barrier materials be placed over the root canal obturation and sodium perborate be used with water rather than with hydrogen peroxide. The purpose of this study was to evaluate the amount of the hydrogen peroxide penetration according to the difference in intracanal base materials and sodium perborate preparation. Fifty extracted intact premolars were instrumented, and filled with gutta-percha. And then the outer surface of the teeth was sealed with wax exposing the CEJ. The prepared teeth were placed in plastic tubes containing 1.5ml distilled water with their entire root submerged into the solution, The teeth were divided into the following five groups. In the first two groups gutta-percha was removed without placement of barrier, and then water or superoxole(30% $H_2O_2$) with sodium perborate were used respectively for bleaching. In the other three groups, after removal of gutta-percha, an intracanal isolating barrier(ZPC, IRM, Fuji II LC) was placed and then bleached with sodium perborate and superoxole. The bleaching procedure was performed 4 times with 1 week interval. The results were as follows : 1. All the groups showed a tendency of increasing penetration amount with increasing treatment times(P<0.05). 2. After the 1st and 2nd treatments, there was no significant difference in microleakage among the groups. 3. After the 3rd bleaching with superoxole and sodium perborate, there was no significant difference in microleakage between gutta-percha alone group and gutta-percha with ZPC, Fuji II LC barrier group. But significant difference was found between IRM barrier group and other groups(P<0.01). 4. After the 4th bleaching with superoxole and sodium perborate, there was no significant difference between gutta-percha alone group and gutta-percha with barrier groups. 5. After the 4th treatment, the group bleached with sodium perborate and water without barrier showed lower hydrogen peroxide penetration than that of other groups(P<0.01).