Among the effects of tooth bleaching on composite resins, degree of color change and dye deposition onto composite resins after office bleaching were investigated in vitro. Seventy two disc-shaped resin samples were fabricated with hybrid type composite resin, Z-100 under 3 different environments(24 samples for each environment) characterized by 3 kinds of light-curing intensity and duration($250mW/cm^2$-20sec., $250mW/cm^2$-40sec., $550mW/cm^2$-20sec.). As control, one-third samples of each group were not treated with bleaching agent. The remaining two-thirds samples of each group were treated with bleaching agent(bleaching group). Then, before thermocycling procedure in coffee bath, the half of the samples treated with bleaching agent were polished(polishing group) with polishing system. SofLex, but the other half(not-polishing group) and control group were not polished. Another 72 samples were also made with microfilled type composite resin. Sillux Plus and treated according to the experimental procedures mentioned above. The color of each resin sample was measured before bleaching, after bleaching, and after thermocycling preceded by bleaching. And color difference was evaluated. It was concluded as follows: 1. The amount of color change of resin samples after office bleaching was not statistically significant(p>0.05). But the samples which were treated with bleaching agent showed more color change than that of control group. 2. After thermocycling in coffee bath, the amount of color change of resin samples between control and bleaching group was not statistically significant(p>0.05). 3. After thermocycling in coffee bath, the polishing procedure of resin samples showed no statistically significant difference(p>0.05) between polishing and not-polishing group in the aspect of color change.