Factors to cause accidents were investigated through a systematic analysis of leakage accidents in welded LP-gas cylinder between 199 and 1999. As a result It was showed that most of leakage accident occurred at the pin-hole due to the localized corrosion on welded zone in cylinder. Accordingly, in this paper, we suggested that the problems of heat treatment condition in two-piece welded cylinder and substitute proposal for preventing the tearing of T zone in three-piece welded cylinder. Furthermore, corrosion rate on the weldment and base metal of welded LP-gas cylinder was evaluated using the electrochemical tests in acid rain and $3.5\%NaCl$ solution, Also, the poor adhesion and defects of film which was produced by electrostatic powder spray painting, while the LP-gas cylinder was manufactured, were analyzed using SEM(Scanning Electron Microscopy). And we proposed a optimum coating thickness of the cylinder.