The physicochemical characteristics such as glass transition temperature (Tg), surface energy, swelling and FT-IR of [P(AA-co-PEGMM)], a copolymer of acrylic acid (AA) and polyethyleneglycol monoethylether mono methacrylate (PEGMM), were evaluated. The Tg of [P(AA-co-PEGMM)] decreased with increasing PEGMM content. [P(AA-co-PEGMM)] with 18 mole% PEGMM had the Tg of about $40^{circ}C$, the similar physiological temperature of human. Moreover, [P(AA-co-PEGMM)] with lower PEGMM content had higher hydration and expected lower mucoadhesive strengths. To predict the mucoadhesiveness of [P(AA-co-PEGMM)] films, the contact angle of films were measured. With the increasing content of PEGMM of films, the contact angle was increased and the higher mucoadhesive forces was expected. ATR-FTIR studies revealed that the addition of the PEG moiety in AA increased the potential of hydrogen bonding for [P(AA-co-PEGMM)] as compared to cross linking polyacrylic acid (cr-PAA) because the oxygen in the repeat unit of PEG contributed in the formation of hydrogen bonding in the presence of mucin solution.