If defects are located far apart, fatigue cracks are independently initiated from them and gradually approach other cracks so that the fatigue life becomes influenced by the crack growth behavior of those interacting cracks. In this study, the effect of the stress interaction between defects on the fatigue crack propagation behavior is investigated experimentally and these results are verified by finite element method. In addition, fatigue crack propagation behaviors under micro hole interaction field are studied.