P(VDF/TrFE) copolymer thin films with 70/30 and 80/20 mol% VDF (polyvinylidene fluoride) and TrFE (trifluoroethylene) rates were prepared by using a vapor deposition method, During thin films were prepared, the substrate temperatures were maintained at 30 $^{circ}C$ and 120 $^{circ}C$, and the heating source temperature was fixed at 350 $^{circ}C$. Contary to PVDF homopolymer, P(VDF/TrFE) copolymers showed the Curie point(Tc) below the melting point. The Curie point (Tc) and the melting point of the P(VDF/TrFE) copolymers were changed as a function of substrate temperature and the VDF mol%. The Curie point and the melting point of P(VDF/TreFE) thin films decreased and increased with increasing substrate temperature, respectively. Also with increasing VDF mol%, the melting point decreased slightly, however the Curie point increased.