Nd0.05Y0.95Ca₄O(BO₃)₃(Nd:YCOB) single crystals were grown by the Czochralski method using a iridium crucible under N₂ atmosphere. Optimum growth parameters to get high quality of single crystals were 1.5∼2 mm/hr of growth rate and 10∼20 rpm of rotation rate. The grown crystals were transparent with light purple color and well-developed in cleavage planes. The crystal structure of Nd;YCOB were identified to monoclinic by XRD method. Crystal defects acting as light scattering centers, such as micro-pores, secondary phases, inclusions and cracks were not observed under the He-Ne laser illuminations. Three red, green, blue laser devices for the RGB laser oscillations were designed and then fabricated from the grown Nd:YCOB crystals according to the phase-matching angles of negative type-I which were φ=16.40°, 33.95° and θ=22.59° with the flatness of λ/6 at least, respectively.