Electrochemically active lithium nickel cobalt oxide thin-film was not fabricated until now. The thin-film was deposited by RF magnetron sputtering at room temperature, and its initial phase was amorphous. By varying deposition condition, the different characteristics of thin-film were achieved. Using electrochemical analyses, the relationship between physical and electrochemical characteristics was identified. Crystallized thin-film by RTA (Rapid Thermal Annealing) was shown a good capacity and cycle property.