The microwave dielectric properties and a sintering behavior of MgTiO$_3$-CaTiO$_3$ ceramics doped with Li were investigated. The main composition was fixed as 0.94MMgTiO$_3$-0.06CaTiO$_3$ and Li$_2$CO$_3$was added excessively in the range of 0~10 mol% (with reference to Li atoms) and the specimens were sintered at 1200~140$0^{circ}C$ for 4 hours. When the amount of Li was small the quality factor and dielectric constant were reduced, while those tow properties increased if the Li amount was above 1 mol%. But if Li was overly added those dielectric properties decreased again. Li, if added in the composition range of 1.0~3.0 mol%, can increase the quality factor of MgTiO$_3$-CaTiO$_3$ ceramics. The optimum amount of Li was 1.5mol% and sinterign condition was 1275$^{circ}C$/4hr, at which we cudl obtain following results ; dielectric constant ($varepsilon$$_{r}$) of f20.0, quality factor(Qxf$_{0}$) of 78,000 GHz and temperature coefficient of resonant frequency($ au$$_{f}$) of -1.6 ppm/$^{circ}C$.>.>.>.