Via for achieving reliable fabrication of MCM(Multichip Module) substrate was formed on photosensitive BCB layer. The MCM substrate consists of photosensitive BCB(Benzocyclobutene) interlayer dielectric and copper conductors. In order to form the vias in the photosensitive BCB layer, the process of forming the BCB layer and its via forming plasma etch using C$_2$F$\_$6//O$_2$ gas were evaluated. The thickness of the BCB layer after hard bake was shrunk down to 40% of the original. The resolution of vias formed on the BCB was 15㎛ and the slope after develop was 85 degree. AES analysis was done on two vias, one is etched in C$_2$F$\_$6/O$_2$ gas and the other isnot etched. On the via etched in C$_2$F$\_$6//O$_2$, native C was detected and the amount of native C was reduced after Ar sputter. On the via not etched in C$_2$F$\_$6//O$_2$, organic C was detected. As a result of AES, BCB residue was not removed by Ar sputter, so plasma etch is necessary for achieving reliable vias.