Glasses in he system CuO-P$_2$O$_{5}$ -Nb$_2$O$_{5}$ -Nb$_2$O$_{5}$ -V$_2$O$_{5}$ were prepared by a press-quenching method on the copper plate. the glass-ceramics from these glasses were obtained by post-heat treatment, and the crystallization behavior and DC conductivities were determined. The conductivities of the glasses were range from 10$^{-6}$ s.$cm^{-1}$ / at room temperature ,but the conductivities of the glass-ceramics were 10$^{-3}$ s.$cm^{-1}$ / increased by 10$^3$ order. The crystalline product in the glass-ceramics was CuV$_2$O$_{6}$ . the crystal growth of CuV$_2$O$_{6}$ phase increased with heat-treatment conditions. The linear relationship between il($sigma$T) and T$^{-1}$ suggested that the electrical conduction in the present glass-ceramics would be due to a small polaron hopping(SPH) mechanism.